ANSI压力温度等级表

ANSI压力温度等级
ANSI Pressure Temperature Ratings

英制单位
ENGLISH UNITS

　　下列压力-温度表来自ANSI B16.34 - 1996版，包含行业内最常用的阀体和阀帽材料。
　　The following pressure-temperature charts are derived from ANSI B16.34 - 1996 Version. It will cover the most commonly-used body and bonnet materials in the Industry.

ASTM A216等级WCB
ASTM A216 GR. WCB

留心：在长时间处于温度超过426oC的环境中，碳钢的碳化物相可能转化为石墨。答应，但是建议不要长时间在温度超过426oC的环境中应用。
NOTE: Upon prolonged exposure to temperatures above 800oF, the carbide phase of carbon steel may be converted to graphite. Permissible, but not recommended for prolonged usage above 800oF.

ASTM A216等级WCC
ASTM A216 GR. WCC

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 400 600 900 1500 2500 4500 150 300 400 600 900 1500 2500 4500 -20 TO 100
200
300 290
260
230 750
750
730 1000
1000
970 1500
1500
1455 2250
2250
2185 3750
3750
3640 6250
6250
6070 11250
11250
10925 290
290
290 750
750
750 1000
1000
1000 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 11250
11250
11250 400
500
600 200
170
140 705
665
605 940
885
805 1410
1330
1210 2115
1995
1815 3530
3325
3025 5880
5540
5040 10585
9965
9070 290
290
290 750
750
750 1000
1000
1000 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 11250
11250
11250 650
700
750
800 125
110
95
80 590
570
505
410 785
755
670
550 1175
1135
1010
825 1765
1705
1510
1235 2940
2840
2520
2060 4905
4730
4200
3430 8825
8515
7560
6170 290
275
240
195 750
710
630
515 1000
950
840
685 1500
1425
1260
1030 2250
2135
1890
1545 3750
3560
3150
2570 6250
5930
5250
4285 11250
10670
9450
7715 850
900
950
1000 65
50
35
20 270
170
105
50 355
230
140
70 535
345
205
105 805
515
310
155 1340
860
515
260 2230
1430
860
430 4010
2750
1545
770 130
80
50
25 335
215
130
65 445
285
170
85 670
430
260
130 1005
645
385
195 1670
1070
645
320 2785
1785
1070
535 5015
3215
1930
965

ASTM A352等级LCB
ASTM A352 GR. LCB

留心：不能用于温度超过343oC.
Note: Not to be used over 650oF.

ASTM A217等级WC6
ASTM A217 GR. WC6

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 450 1125 2250 3375 5625 9375 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 825 1650 2475 4125 6875 325 825 1650 2475 4125 6875 -20 TO 100
200
300 290
260
230 750
750
720 1500
1500
1445 2250
2250
2165 3750
3750
3610 6250
6250
6015 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 400
500
600 200
170
140 695
665
605 1385
1330
1210 2080
1995
1815 3465
3325
3025 5775
5540
5040 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 650
700
750 125
110
95 590
570
530 1175
1135
1065 1765
1705
1595 2940
2840
2660 4905
4730
4430 290
280
280 750
735
730 1500
1465
1460 2250
2200
2185 3750
3665
3645 6250
6110
6070 800
850
900 80
65
50 510
485
450 1015
975
900 1525
1460
1350 2540
2435
2245 4230
4060
3745 275
260
225 720
680
585 1440
1355
1175 2160
2030
1760 3600
3385
2935 6000
5645
4895 950
1000
1050 35
20
20(1) 320
215
145 640
430
290 955
650
430 1595
1080
720 2655
1800
1200 155
105
70 400
270
180 795
540
360 1195
810
540 1995
1350
900 3320
2250
1500 1100 20(1) 95 190 290 480 800 45 120 240 360 600 1000

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC. 不能用于温度超过593oC的环境中。
Note: (1) For weld end valves only. Flanged end ratings terminate at 1000oF. Must not be used over 1100oF.

ASTM A217等级WC9
ASTM A217 GR. WC9

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 450 1125 2250 3375 5625 9375 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 825 1650 2475 4125 6875 325 825 1650 2475 4125 6875 -20 TO 100
200
300 290
260
230 750
750
730 1500
1500
1455 2250
2250
2185 3750
3750
3640 6250
6250
6070 290
290
285 750
750
740 1500
1500
1485 2250
2250
2225 3750
3750
3705 6250
6250
6180 400
500
600 200
170
140 705
665
605 1410
1330
1210 2115
1995
1815 3530
3325
3025 5880
5540
5040 280
275
275 725
720
720 1450
1440
1440 2175
2160
2160 3620
3600
3600 6035
6000
6000 650
700
750 125
110
95 590
570
530 1175
1135
1065 1765
1705
1595 2940
2840
2660 4905
4730
4430 275
275
265 715
710
690 1430
1425
1380 2145
2135
2070 3580
3555
3450 5965
5930
5750 800
850
900 80
65
50 510
485
450 1015
975
900 1525
1460
1350 2540
2435
2245 4230
4060
3745 260
245
230 675
645
600 1345
1285
1200 2020
1930
1800 3365
3215
3000 5605
5355
5000 950
1000
1050 35
20
20(1) 375
260
175 755
520
350 1130
780
525 1885
1305
875 3145
2170
1455 180
125
85 470
325
220 945
650
435 1415
975
655 2355
1630
1095 3930
2715
1820 1100 20(1) 110 220 330 550 915 55 135 275 410 685 1145

ASTM A217等级C5
ASTM A217 GR. C5

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 450 1125 2250 3375 5625 9375 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 825 1650 2475 4125 6875 325 825 1650 2475 4125 6875 -20 TO 100
200
300 290
260
230 750
745
715 1500
1490
1430 2250
2235
2150 3750
3725
3580 6250
6205
5965 290
290
280 750
750
730 1500
1500
1455 2250
2250
2185 3750
3750
3645 6250
6250
6070 400
500
600 200
170
140 705
665
605 1410
1330
1210 2115
1995
1815 3530
3325
3025 5880
5540
5040 275
275
270 720
720
705 1440
1440
1415 2160
2160
2120 3600
3600
3535 6000
6000
5895 650
700
750 125
110
95 590
570
530 1175
1135
1055 1765
1705
1585 2940
2840
2640 4905
4730
4400 270
265
255 700
685
660 1395
1370
1320 2095
2055
1980 3495
3430
3300 5820
5715
5500 800
850
900 80
65
50 510
485
370 1015
965
740 1525
1450
1110 2540
2415
1850 4230
4030
3085 245
230
175 640
605
465 1275
1210
925 1915
1815
1390 3195
3020
2315 5320
5035
3855 950
1000
1050 35
20
20(1) 275
200
145 550
400
290 825
595
430 1370
995
720 2285
1655
1200 130
95
70 345
250
180 685
495
360 1030
745
540 1715
1245
900 2855
2070
1500 1100
1150
1200 20(1)
20(1)
15(1) 100
60
35 200
125
70 300
185
105 495
310
170 830
515
285 50
30
15 125
75
45 250
155
85 375
230
130 620
385
215 1035
645
355

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC.
Note: (1) For weld end valves only. Flanged end ratings terminate at 1000oF.

ASTM A217等级C12
ASTM A217 GR. C12

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 450 1125 2250 3375 5625 9375 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 825 1650 2475 4125 6875 325 825 1650 2475 4125 6875 -20 TO 100
200
300 290
260
230 750
750
730 1500
1500
1455 2250
2250
2185 3750
3750
3640 6250
6250
6070 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 400
500
600 200
170
140 705
665
605 1410
1330
1210 2115
1995
1815 3530
3325
3025 5880
5540
5040 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 650
700
750 125
110
95 590
570
530 1175
1135
1065 1765
1705
1595 2940
2840
2660 4905
4730
4430 290
280
280 750
735
730 1500
1465
1460 2250
2200
2185 3750
3655
3645 6250
6110
6070 800
850
900 80
65
50 510
485
450 1015
975
900 1525
1460
1350 2540
2435
2245 4230
4060
3745 275
260
230 720
680
600 1440
1355
1200 2160
2030
1800 3600
3385
3000 6000
5645
5000 950
1000
1050 35
20
20(1) 375
255
170 755
505
345 1130
760
515 1885
1270
855 3145
2115
1430 180
120
80 470
315
215 945
635
430 1415
950
645 2355
1585
1070 3930
2645
1785 1100
1150
1200 20(1)
20(1)
20(1) 115
75
50 225
150
105 340
225
155 565
375
255 945
630
430 55
35
25 140
95
65 285
190
130 425
285
195 710
470
320 1180
785
535

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC.
Note: (1) For weld end valves only. Flanged end ratings terminate at 1000oF.

ASTM A351等级CF8M
ASTM A351 GR. CF8M

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 425 1100 2175 3250 5400 9000 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 800 1600 2400 3975 6600 325 825 1650 2475 4125 6875 -20 TO 100
200
300 275
215
195 720
620
560 1440
1240
1120 2160
1860
1680 3600
3095
2795 6000
5160
4660 290
265
240 750
690
625 1500
1380
1250 2250
2070
1870 3750
3450
3120 6250
5750
5200 400
500
600 170
140
125 515
480
450 1025
955
900 1540
1435
1355 2570
2390
2255 4280
3980
3760 220
205
195 570
530
505 1140
1065
1005 1710
1595
1510 2850
2655
2520 4750
4430
4195 650
700
750 110
95
80 445
430
425 890
870
855 1330
1305
1280 2220
2170
2135 3700
3620
3560 190
185
180 495
485
475 985
970
950 1480
1455
1425 2465
2420
2380 4105
4035
3965 800
850
900 65
50
35 420
420
415 845
835
830 1265
1255
1245 2110
2090
2075 3520
3480
3460 180
180
175 470
465
465 945
930
925 1415
1400
1390 2355
2330
2315 3930
3885
3855 950
1000
1050 20
20
20(1) 385
350
345 775
700
685 1160
1050
1030 1930
1750
1720 3220
2915
2865 175
160
160 460
420
420 915
840
840 1375
1260
1260 2290
2105
2105 3815
3505
3505 1100
1150
1200
1250
1300 20(1)
20(1)
20(1)
20(1)
20(1) 305
235
185
145
115 610
475
370
295
235 915
710
555
440
350 1525
1185
925
735
585 2545
1970
1545
1230
970 145
115
90
70
55 380
295
230
185
145 765
590
465
370
290 1145
885
695
555
435 1905
1480
1155
920
730 3180
2465
1930
1535
1215 1350
1400
1450
1500 20(1)
20(1)
20(1)
20(1) 95
75
60
40 190
150
115
85 290
225
175
125 480
380
290
205 800
630
485
345 45
35
30
20 120
95
75
50 240
190
145
105 360
285
200
155 600
470
365
260 1000
785
610
430

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC. 当温度超过537oC时，只能采用碳含量超过0.04%的材料的阀门。
Notes: (1) For weld end valves only. Flanged end ratings terminate at 1000oF. At temperatures over 1000oF, use only when the carbon content is 0.04% or higher.

ASTM A351等级CF8C
ASTM A351 GR. CF8C

华氏度
oF 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 425 1080 2175 3250 5400 9000 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 800 1600 2400 3975 6600 325 825 1650 2475 4125 6875 -20 TO 100
200
300 275
255
230 720
660
615 1440
1320
1230 2160
1980
1845 3600
3300
3070 6000
5500
5120 290
275
250 750
715
655 1500
1430
1310 2250
2145
1965 3750
3580
3280 6250
5965
5465 400
500
600 200
170
140 575
540
515 1145
1080
1025 1720
1620
1540 2870
2700
2570 4780
4500
4280 235
230
220 615
595
575 125
1190
1145 1850
1785
1720 3085
2980
2865 5145
4965
4775 650
700
750 125
110
95 505
495
490 1010
990
985 1510
1485
1475 2520
2470
2460 4200
4120
4100 215
210
210 565
550
550 1125
1105
1095 1690
1655
1645 2815
2760
2745 4690
4600
4570 800
850
900 80
65
50 485
485
450 975
970
900 1460
1455
1350 2435
2425
2245 4060
4040
3745 210
205
205 545
540
540 1090
1080
1075 1630
1625
1615 2720
2705
2690 4530
4510
4485 950
1000
1050 35
20
20(1) 385
365
360 775
725
720 1160
1090
1080 1930
1820
1800 3220
3030
3000 180
160
160 470
420
420 945
840
840 1415
1260
1260 2360
2105
2105 3930
3505
3505 1100
1150
1200
1250
1300 20(1)
20(1)
20(1)
20(1)
20(1) 325
275
170
125
95 645
550
345
245
185 965
825
515
370
280 1316
1370
855
615
465 2685
2285
1430
1030
770 155
130
80
60
45 405
345
215
155
115 805
685
430
310
230 1210
1030
645
465
345 2015
1715
1070
770
580 3360
2855
1785
1285
965 1350
1400
1450
1500 20(1)
20(1)
20(1)
20(1) 70
55
40
35 135
110
80
70 205
165
125
105 345
275
205
170 570
455
345
285 35
25
20
15 85
70
50
45 170
135
105
85 255
205
155
130 430
345
255
215 715
570
430
355

英制单位
ENGLISH UNITS

　　相当于ASTM A182等级F91，经过改良的9Cr-Mo-V铸件材料的额定压力温度，目前还没有列在ANSI B16.34 - 1996年版本中。在升高的温度下，这种材料的答应应力值已经颁布在《ASME规程案例2192，1995年三月》中。利用《规程案例2192》中的答应应力值，及ANSI B16.34，附录F中先容的方法，ASTM A217等级C12A的额定压力-温度的盘算值以下表列出。
　　Pressure Temperature Ratings for modified 9Cr-Mo-V Cast Material equivalent to ASTM A182, GR. F91 are not currently listed in ANSI B-16.34 - 1996 version. Allowable stress values for this material at elevated temperatures were published in ASME Code Case 2192, March 1995. Using the allowable stress valves in Code Case 2192, and the methods outlined in ANSI B16.34, Annex F, the calculated values for Pressure-Temperature Ratings ASTM A217, GR. C12A are tabulated below.

ASTM A217等级C12A
ASTM A217 GR. C12A

华氏度
oF 尺度等级
STANDARD CLASS 特别等级
SPECIAL CLASS 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 最大非冲击工作压力，PSIG
MAXIMUM NON-SHOCK WORKING PRESSURE, PSIG 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 450 1125 2250 3375 5625 9375 450 1125 2250 3375 5625 9375 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 325 825 1650 2475 4125 6875 325 825 1650 2475 4125 6875 -20 TO 100
200
300 290
260
230 750
750
730 1500
1500
1455 2250
2250
2185 3750
3750
3640 6250
6250
6070 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 400
500
600 200
170
140 705
665
605 1410
1330
1210 2115
1995
1815 3530
3325
3025 5880
5540
5040 290
290
290 750
750
750 1500
1500
1500 2250
2250
2250 3750
3750
3750 6250
6250
6250 650
700
750 125
110
95 590
570
530 1175
1135
1065 1765
1705
1595 2940
2840
2660 4905
4730
4430 290
280
280 750
735
730 1500
1465
1460 2250
2200
2185 3750
3665
3645 6250
6110
6070 800
850
900 80
65
50 510
485
450 1015
975
900 1525
1460
1350 2540
2435
2245 4230
4060
3745 275
260
230 720
680
600 1440
1355
1200 2160
2030
1800 3600
3385
3000 6000
5645
5000 950
1000
1050 35
20
20 385
365
360 775
725
720 1160
1090
1080 1930
1820
1800 3220
3030
3000 180
160
160 470
420
420 945
840
840 1415
1260
1260 2360
2105
2105 3930
3505
3505 1100
1150
1200 20
20
20 300
225
145 605
445
290 905
670
430 1510
1115
720 2515
1855
1200 145
105
70 375
280
180 755
555
360 1130
835
540 1885
1395
900 3145
2320
1500

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度最高为537oC.
Notes: (1) For weld end valves only. Flanged end ratings terminate at 1000oF.

公制单位
METRIC UNITS

　　下列压力-温度表来自ANSI B16.34 - 1996版，包含行业内最常用的阀体和阀帽材料。
　　所有美国太平洋阀门都实用于这些压力-温度表内某个特定的ANSI压力等级和ASTM材料所显示的压力和温度范畴内。作为尺度，美国太平洋阀门所进行的流体静力学壳体检测压力是ANSI额定压力等级的最大冷冲击工作压力的1.5倍，流体静力学阀座检测压力是是ANSI额定压力等级的最大冷冲击工作压力的1.1倍。
　　The following pressure-temperature charts are derived from ANSI B16.34 - 1996 Version. It will cover the most commonly-used body and bonnet materials in the Industry.
　　All Pacific Valves are designed to operate through pressure and temperature range shown in these P-T Charts for a particular ANSI Class Rating and ASTM Material. As a standard, Pacific Valves performs Hydrostatic Shell Testing at a minimum 1.5 times and Hydrostatic Seat Testing at a minimum of 1.1 times the Maximum Cold Working Pressure of an ANSI Class Rating.

ASTM A216等级WCB
ASTM A216 GR. WCB

留心：在长时间处于温度超过426oC的环境中，碳钢的碳化物相可能转化为石墨。答应，但是建议不要长时间在温度超过426oC的环境中应用。
Note: Upon prolonged exposure to temperatures above 427oC, the carbide phase of carbon steel may be converted to graphite. Permissible, but not recommended for prolonged usage above 427oC.

ASTM A216等级WCC
ASTM A216 GR. WCC

ASTM A352等级LCB
ASTM A352, GR. LCB

留心：不能用于温度超过343oC.
Note: Not to be used over 343oC

ASTM A217等级WC6
ASTM A217 GR. WC6

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 3103 7756 15513 23269 38782 64637 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5688 11376 17064 28440 47401 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1999
1793
1586 5171
5171
4964 10342
10342
9963 15513
15513
14927 25855
25855
24890 43092
43092
41471 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 204
260
316 1379
1172
965 4792
4585
4171 9549
9170
8343 14341
13755
12514 23890
22925
20856 39817
38196
34749 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 343
371
399 862
758
655 4068
3930
3654 8101
7825
7343 12169
11755
10997 20270
19581
18340 33818
32612
30543 1999
1931
1931 5171
5068
5033 10342
10101
10066 15513
15168
15065 25855
25269
25131 43092
42126
41851 427
454
482 552
448
345 3516
3344
3103 6998
6722
6205 10514
10066
9308 17512
16788
15478 29164
27992
25820 1896
1793
1551 4964
4688
4033 9928
9342
8101 14892
13996
12135 24821
23338
20236 41368
38920
33749 510
538
566 241
138
138(1) 2206
1482
1000 4413
2965
1999 6584
4482
2965 10997
7446
4964 18305
12410
8274 1069
724
483 2758
1862
1241 5481
3723
2482 8239
5585
3723 13755
9308
6205 22890
15513
10342 593 138(1) 655 1310 1999 3309 5516 310 827 1655 2482 4137 6895

留心：(1) (1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC. 不能用于温度超过593oC的环境中。
Note: (1) For weld end valves only. Flanged end ratings terminate at 538oC. Must not be used over 593oC.

ASTM A217等级WC9
ASTM A217 GR. WC9

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 3103 7756 15513 23269 38782 64637 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5688 11376 17064 28440 47401 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1999
1793
1586 5171
5171
5033 10342
10342
10032 15513
15513
15065 25855
25855
25097 43092
43092
41851 1999
1999
1965 5171
5171
5102 10342
10342
10239 15513
15513
15341 25855
25855
25545 43092
43092
42609 204
260
316 1379
1172
965 4861
4585
4171 9721
9170
8343 14582
13755
12514 24338
22925
20856 40541
38196
34749 1931
1896
1896 4999
4964
4964 9997
9928
9928 14996
14892
14892 24959
24821
24821 41609
41368
41368 343
371
399 862
758
655 4068
3930
3654 8101
7825
7343 12169
11755
10997 20270
19581
18340 33818
32612
30543 1896
1896
1827 4930
4895
4757 9859
9825
9515 14789
14720
14272 24683
24510
23787 41127
40885
39644 427
454
482 552
448
345 3516
3344
3103 6998
6722
6205 10514
10066
9308 17512
16788
15478 29164
27992
25820 1793
1689
1586 4654
4447
4137 9273
8860
8274 13927
13307
12410 23200
22166
20684 38645
36921
34473 510
538
566 241
138
138(1) 2585
1793
1207 5205
3585
2413 7791
5378
3620 12996
8998
6033 21684
14961
10032 1241
862
586 3240
2241
1517 6515
4482
2999 9756
6722
4516 16237
11238
7550 27096
18719
12548 593 138(1) 758 1517 2275 3792 6309 379 931 1896 2827 4723 7894

ASTM A217等级C5
ASTM A217 GR. C5

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 3103 7756 15513 23269 38782 64637 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5688 11376 17064 28440 47401 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1999
1793
1586 5171
5137
4930 10342
10273
9859 15513
15410
14823 25855
25683
24683 43092
42781
41127 1999
1999
1931 5171
5171
5033 10342
10342
10032 15513
15513
15065 25855
25855
25131 43092
43092
41851 204
260
316 1379
1172
965 4861
4585
4171 9721
9170
8343 14582
13755
12514 24338
22925
20856 40541
38196
34749 1896
1896
1862 4964
4964
4861 9928
9928
9756 14892
14892
14617 24821
24821
24373 41368
41368
40644 343
371
399 862
758
655 4068
3930
3654 8101
7825
7274 12169
11755
10928 20270
19581
18202 33818
32612
30336 1862
1827
1758 4826
4723
4550 9618
9446
9101 14444
14169
13651 24097
23649
22752 40127
39403
37921 427
454
482 552
448
345 3516
3344
2551 6998
6653
5102 10514
9997
7653 17512
16651
12755 29164
27785
21270 1689
1586
1207 4413
4171
3206 8791
8343
6378 13203
12514
9584 22028
20822
15961 36680
34715
26579 510
538
566 241
138
138(1) 1896
1379
1000 3792
2758
1999 5688
4102
2965 9446
6860
4964 15754
11411
8274 896
655
483 2379
1724
1241 4723
3413
2482 7101
5137
3723 11824
8584
6205 19684
14272
10342 593
621
649 138(1)
138(1)
138(1) 689
414
241 1379
862
483 2068
1276
724 3413
2137
1172 5723
3551
1965 345
207
103 862
517
310 1724
1069
586 2585
1586
896 4275
2654
1482 7136
4447
2448

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC.
Notes: (1) For weld end valves only. Flanged end ratings terminate at 538oC.

ASTM A217等级C12
ASTM A217 GR. C12

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 3103 7756 15513 23269 38782 64637 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5688 11376 17064 28440 47401 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1999
1793
1586 5171
5171
5033 10342
10342
10032 15513
15513
15065 25855
25855
25097 43092
43092
41851 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 204
260
316 1379
1172
965 4861
4585
4171 9721
9170
8343 14582
13755
12514 24338
22925
20856 40541
38196
34749 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 343
371
399 862
758
655 4068
3930
3654 8101
7825
7343 12169
11755
10997 20270
19581
18340 33818
32612
30543 1999
1931
1931 5171
5068
5033 10342
10101
10066 15513
15168
15065 25855
25200
25131 43092
42126
41851 427
454
482 552
448
345 3516
3344
3103 6998
6722
6205 10514
10066
9308 17512
16788
15478 29164
27992
25820 1896
1793
1586 4964
4688
4137 9928
9342
8274 14892
13996
12410 24821
23338
20684 41368
38920
34473 510
538
566 241
138
138(1) 2585
1758
1172 5205
3482
2379 7791
5240
3551 12996
8756
5895 21684
14582
9859 1241
827
552 3240
2172
1482 6515
4378
2965 9756
6550
4447 16237
10928
7377 27096
18236
12307 593
621
649 138(1)
138(1)
138(1) 793
517
345 1551
1034
724 2344
1551
1069 3895
2585
1758 6515
4344
2965 379
241
172 965
655
448 1965
1310
896 2930
1965
1344 4895
3240
2206 8136
5412
3689

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC.
Notes: (1) For weld end valves only. Flanged end ratings terminate at 538oC.

ASTM A351等级CF8M
ASTM A351 GR. CF8M

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 2930 7584 14996 22408 37231 62052 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5516 11031 16547 27406 45505 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1896
1482
1344 4964
4275
3861 9928
8549
7722 14892
12824
11583 24821
21339
19271 41368
35576
32129 1999
1827
1655 5171
4757
4309 10342
9515
8618 15513
14272
12893 25855
23787
21511 43092
39644
35852 204
260
316 1172
965
862 3551
3309
3103 7067
6584
6205 10618
9894
9342 17719
16478
15547 29509
27441
25924 1517
1413
1344 3930
3654
3482 7860
7343
6929 11790
10997
10411 19650
18305
17375 32750
30543
28923 343
371
399 758
655
552 3068
2965
2930 6136
5998
5895 9170
8998
8825 15306
14961
14720 25510
24959
24545 1310
1276
1241 3413
3344
3275 6791
6688
6550 10204
10032
9825 16995
16685
16409 28303
27820
27337 427
454
482 448
345
241 2896
2896
2861 5826
5757
5723 8722
8653
8584 14548
14410
14306 24269
23993
23855 1241
1241
1207 3240
3206
3206 6515
6412
6378 9756
9653
9584 16237
16065
15961 27096
26786
26579 510
538
566 138
138
138(1) 2654
2413
2379 5343
4826
4723 7998
7239
7101 13307
12066
11859 22201
20098
19753 1207
1103
1103 3172
2896
2896 6309
5792
5792 9480
8687
8687 15789
14513
14513 26303
24166
24166 593
621
649 138(1)
138(1)
138(1) 2103
1620
1276 4206
3275
2551 6309
4895
3827 10514
8170
6378 17547
13582
10652 1000
793
621 2620
2034
1586 5274
4068
3206 7894
6102
4792 13134
10204
7963 21925
16995
13307 677
704
732 138(1)
138(1)
138(1) 1000
793
655 2034
1620
1310 3034
2413
1999 5068
4033
3309 8480
6688
5516 483
379
310 1276
1000
827 2551
1999
1655 3827
2999
2482 6343
5033
4137 10583
8377
6895 760
788
816 138(1)
138(1)
138(1) 517
414
276 1034
793
586 1551
1207
862 2620
1999
1413 4344
3344
2379 241
207
138 655
517
345 1310
1000
724 1965
1379
1069 3240
2517
1793 5412
4206
2965

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度为537oC. 当温度超过537oC时，只能采用碳含量超过0.04%的材料的阀门。
Notes: (1) For weld end valves only. Flanged end ratings terminate at 538oC. At temperatures over 538oC, use only when the carbon content is 0.04% or higher.

ASTM A351等级CF8C
ASTM A351 GR. CF8C

摄氏度
oC 尺度等级B16.34 - 1996
STANDARD CLASS B16.34 - 1996 特别等级B16.34 - 1996
SPECIAL CLASS B16.34 - 1996 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 2930 7446 14996 22408 37231 62052 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5516 11031 16547 27406 45505 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1896
1758
1586 4964
4550
4240 9928
9101
8480 14892
13651
12721 24821
22752
21167 41368
37921
35301 1999
1896
1724 5171
4930
4516 10342
9859
9032 15513
14789
13548 25855
24683
22614 43092
41127
37679 204
260
316 1379
1172
965 3964
3723
3551 7894
7446
7067 11859
11169
10618 19788
18616
17719 32956
31026
29509 1620
1586
1517 4240
4102
3964 862
8205
7894 12755
12307
11859 21270
20546
19753 35473
34232
32922 343
371
399 862
758
655 3482
3413
3378 6964
6826
6791 10411
10239
10170 17375
17030
16961 28958
28406
28268 1482
1448
1448 3895
3792
3792 7756
7619
7550 11652
11411
11342 19408
19029
18926 32336
31715
31509 427
454
482 552
448
345 3344
3344
3103 6722
6688
6205 10066
10032
9308 16788
16720
15478 27992
27854
25820 1448
1413
1413 3758
3723
3723 7515
7446
7412 11238
11204
11135 18753
18650
18547 31233
31095
30923 510
538
566 241
138
138(1) 2654
2517
2482 5343
4999
4964 7998
7515
7446 13307
12548
12410 22201
20891
20684 1241
1103
1103 3240
2896
2896 6515
5792
5792 9756
8687
8687 16271
14513
14513 27096
24166
24166 593
621
649
677
704 138(1)
138(1)
138(1)
138(1)
138(1) 2241
1896
1172
862
655 4447
3792
2379
1689
1276 6653
5688
3551
2551
1931 9073
9446
5895
4240
3206 18512
15754
9859
7101
5309 1069
896
552
414
310 2792
2379
1482
1069
793 5550
4723
2965
2137
1586 8343
7101
4447
3206
2379 13893
11824
7377
5309
3999 23166
19684
12307
8860
6653 732
760
788
816 138(1)
138(1)
138(1)
138(1) 483
379
276
241 931
758
552
483 1413
1138
862
724 2379
1896
1413
1172 3930
3137
2379
1965 241
172
138
103 586
483
345
310 1172
931
724
586 1758
1413
1069
896 2965
2379
1758
1482 4930
3930
2965
2448

公制单位
METRIC UNITS

ASTM A217等级C12A
ASTM A217 GR. C12A

摄氏度
oC 尺度等级
STANDARD CLASS 特别等级
SPECIAL CLASS 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 最大非冲击工作压力，KPa
MAXIMUM NON-SHOCK WORKING PRESSURE, kPa 150 300 600 900 1500 2500 150 300 600 900 1500 2500 流体静力学
壳体检测
HYDROSTATIC
SHELL TEST 3103 7756 15513 23269 38782 64637 3103 7756 15513 23269 38782 64637 流体静力学
密封检测
HYDROSTATIC
SEAT TEST 2241 5688 11376 17064 28440 47401 2241 5688 11376 17064 28440 47401 -29 to 38
93
149 1999
1793
1586 5171
5171
5033 10342
10342
10032 15513
15513
15065 25855
25855
25097 43092
43092
41851 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 204
260
316 1379
1172
965 4861
4585
4171 9721
9170
8343 14582
13755
12514 24338
22925
20856 40541
38196
34749 1999
1999
1999 5171
5171
5171 10342
10342
10342 15513
15513
15513 25855
25855
25855 43092
43092
43092 343
371
399 862
758
655 4068
3930
3654 8101
7825
7343 12169
11755
10997 20270
19581
18340 33818
32612
30543 1999
1931
1931 5171
5068
5033 10342
10101
10066 15513
15168
15065 25855
25269
25131 43092
42126
41851 427
454
482 552
448
345 3516
3344
3103 6998
6722
6205 10514
10066
9308 17512
16788
15478 29164
27992
25820 1896
1793
1586 4964
4688
4137 9928
9342
8274 14892
13996
12410 24821
23338
20684 41368
38920
34473 510
538
566 241
138
138 2654
2517
2482 5343
4999
4964 7998
7515
7446 13307
12548
12410 22201
20891
20684 1241
1103
1103 3240
2896
2896 6515
5792
5792 9756
8687
8687 16271
14513
14513 27096
24166
24166 593
621
649 138
138
138 2068
1551
1000 4171
3068
1999 6240
4619
2965 10411
7688
4964 17340
12790
8274 1000
724
483 2585
1931
1241 5205
3827
2482 7791
5757
3723 12996
9618
6205 21684
15996
10342

留心：(1) 仅实用于焊接端口阀门。法兰端口额定温度最高为537oC.
Notes: (1) For weld end valves only. Flanged end ratings terminate at 538oC.